Easy-to-print materials for everyday functional parts, with better toughness, heat resistance or speed.
Typical values. Refer to the actual TDS.
| Compare | Model | Nozzle temperature | Bed temperature | Print speed | Fan | Enclosed chamber | Drying before printing | Hardened steel nozzle | DensityISO 1183 | Tensile strengthISO 527-2 · Printed specimen, XY | Heat deflection temperature (HDT)ISO 75 · 0.45 MPa | Note | Diameter | Net weight | Standard colors | Uses |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| PLA High SpeedGRN3D-PLA-H01 | 200–230 °C | 50–65 °C | 50–300 mm/s | 100 % | Not needed | If damp: 50–55 °C / 4–6 h | Not needed | 1.20–1.26 g/cm³ | 40–55 MPa | 52–58 °C | — | 1.75 mm | 1 kg | 1001 White, 1003 Grey, 1101 Black, 2001 Red, 6001 Blue | Batch printing, rapid prototyping | |
| PLA ToughenedGRN3D-PLA-T01 | 200–230 °C | 45–65 °C | 50–250 mm/s | 100 % | Not needed | 50–55 °C / 6–8 h | Not needed | 1.20–1.26 g/cm³ | 40–55 MPa | 52–60 °C | — | 1.75 mm | 1 kg | 1001 White, 1003 Grey, 1101 Black, 6001 Blue | Snap fits, brackets, fixtures | |
| PLA LightweightGRN3D-PLA-L01 | 200–260 °C (higher temperature, more foaming) | 50–60 °C | 30–100 mm/s | 50–100 % | Not needed | 50–55 °C / 6–8 h | Not needed | Printed part 0.6–1.0 g/cm³ (depends on temperature) | 15–30 MPa | — | Foaming varies with nozzle temperature | 1.75 mm | 0.8 kg | 1001 White, 1101 Black, 1003 Grey | Model aircraft, lightweight models | |
| PETG BasicGRN3D-PETG-S01 | 220–250 °C | 70–85 °C | 40–150 mm/s | 30–60 % | Not needed | 60–65 °C / 6–8 h | Not needed | 1.25–1.29 g/cm³ | 40–55 MPa | 65–75 °C | — | 1.75 mm | 1 kg | 9001 Clear, 1001 White, 1101 Black, 1003 Grey, 6001 Blue, 2001 Red | Utility parts, storage items, indoor functional parts | |
| PETG High SpeedGRN3D-PETG-H01 | 230–260 °C | 70–85 °C | 50–300 mm/s | 30–60 % | Not needed | 60–65 °C / 6–8 h | Not needed | 1.25–1.29 g/cm³ | 40–55 MPa | 65–72 °C | — | 1.75 mm | 1 kg | 1001 White, 1101 Black, 1003 Grey, 6001 Blue | Batch functional parts | |
| ABSGRN3D-ABS-E01 | 230–260 °C | 90–110 °C | 40–150 mm/s | 0–30 % | Recommended | 70–80 °C / 4–6 h | Not needed | 1.03–1.06 g/cm³ | 30–45 MPa | 85–100 °C | — | 1.75 mm | 1 kg | 1001 White, 1101 Black, 1003 Grey | Functional prototypes, housings | |
| ASA BasicGRN3D-ASA-S01 | 240–270 °C | 90–110 °C | 40–150 mm/s | 0–30 % | Recommended | 80 °C / 6–8 h | Not needed | 1.05–1.08 g/cm³ | 35–50 MPa | 90–100 °C | — | 1.75 mm | 1 kg | 1001 White, 1101 Black, 1003 Grey | Outdoor parts, in-car accessories |
GRN3D-PLA-H01
For high-speed printers
GRN3D-PLA-T01
Tougher than standard PLA, less brittle
GRN3D-PLA-L01
Foams during printing, lighter parts
GRN3D-PETG-S01
Good toughness, durable
GRN3D-PETG-H01
For high-speed printers
GRN3D-ABS-E01
Heat resistant, impact resistant
GRN3D-ASA-S01
Weather resistant, color-stable outdoors
Typical values. Refer to the actual TDS. Parameters: to be corrected by GREENPOLYMER. GREENPOLYMER test data: to be verified by GREENPOLYMER.
Standard diameter 1.75 mm; 2.85 mm on request. Diameter tolerance ±0.03 mm (to be verified by GREENPOLYMER). Other colors available as OEM custom colors.
PLA High Speed and PETG High Speed suit high-speed printers; on standard printers, use them at normal speeds.
PLA Toughened is for parts that must withstand bending or repeated snap-fit assembly.
PLA Lightweight saves weight by foaming during printing. Print a temperature tower first to find the weight and surface you need.
Print ABS and ASA in an enclosed chamber to reduce warping and cracking; ventilate while printing.
ASA suits outdoor use; its color is more stable in sunlight than ABS.
Tell us about the part, material requirements, equipment and expected volume. We will recommend suitable grades and the validation data you need.