PC compounds
GL2009U
- Prefix GL
- General purpose (single resin, unfilled, non-flame-retardant)
- Series 2
- PC
- Filler 0
- Unfilled
- MVR 09
- 9 · 300 °C / 1.2 kg
- Property U
- UV-stabilized / weather resistant
PC (UV-stabilized, MVR 9)
- Planned grade
- Available
- GREENPOLYMER TDS
- V-2 @ 0.75 mmUL 94
- 9 cm³/10 minMelt volume-flow rate (MVR) · 300 °C / 1.2 kg
- 120–128 °CHDT · 1.80 MPa
Datasheet
Each value is shown with its test standard and conditions.
- DensityISO 11831.19–1.21g/cm³
- Melt volume-flow rate (MVR)ISO 1133 · 300 °C / 1.2 kg9cm³/10 min
- Tensile stress at yieldISO 527-1/-262–68MPa
- Tensile modulusISO 527-1/-22.3–2.5GPa
- Charpy notched impact strengthISO 179-1/1eA · 23 °C60–80 (partial break)kJ/m²
- Charpy notched impact strengthISO 179-1/1eA · −30 °C10–20kJ/m²
- Heat deflection temperatureISO 75-1/-2 · 1.80 MPa120–128°C
- Heat deflection temperatureISO 75-1/-2 · 0.45 MPa≈ 137°C
- Vicat softening temperatureISO 306 · B120143–148°C
- Moisture absorptionISO 62 · 23 °C / 50 % RH equilibrium≈ 0.12%
- Elongation at breakISO 527-1/-2 · 50 mm/min> 50%
- Flexural modulusISO 1782.3–2.4GPa
- Flexural strengthISO 178≈ 96MPa
Flammability · UL 94Thickness (mm)
| 0.75 | 1.0 | 1.2 | 1.5 | 2.0 | 3.0 | |
|---|---|---|---|---|---|---|
| V-2 | V-2 @ 0.75 mm |
Typical values; not for use as specifications.
Processing window
- Drying120 °C, 2–4 h, desiccant dryer
- Mold temperature80–120 °C
- Melt temperature280–320 °C
- ≤ 0.02 %Max. moisture before processing
- 0.6–0.8 %Molding shrinkage
Colors
Colors
Transparent or opaque; matched to customer color standards
Description
General-purpose polycarbonate balancing toughness, heat resistance and dimensional stability, for transparent or opaque parts. UV-stabilized for outdoor or light-exposed parts. Flow: MVR 9 cm³/10 min (300 °C / 1.2 kg).
Key points
Used for
Other grades in this family
- GL2009General-purpose PC (MVR 9)
- GL2019General-purpose PC (MVR 19)
- GL2019UPC (UV-stabilized, MVR 19)
- FR1009Halogen-free flame-retardant PC (MVR 9)
- FR1009UHalogen-free flame-retardant PC (UV-stabilized)
- FR1009L20Halogen-free flame-retardant PC (−20 °C low-temperature impact, MVR 9)
- FR1009L40Halogen-free flame-retardant PC (−40 °C low-temperature impact)
- FR1015Halogen-free flame-retardant PC (MVR 15)
- FR1015L20Halogen-free flame-retardant PC (−20 °C low-temperature impact, MVR 15)
- FR1004Halogen-free flame-retardant PC (MVR 4)
- FR111010 % glass-fiber-reinforced halogen-free flame-retardant PC
- FR1110U10 % glass-fiber-reinforced halogen-free flame-retardant PC (UV-stabilized)
- FR1110F10 % glass-fiber-reinforced halogen-free flame-retardant PC (improved flow)
- FR1110HF10 % glass-fiber-reinforced halogen-free flame-retardant PC (high flow)
- FR112020 % glass-fiber-reinforced halogen-free flame-retardant PC
- FR113030 % glass-fiber-reinforced halogen-free flame-retardant PC
- FR114040 % glass-fiber-reinforced halogen-free flame-retardant PC
- GF2120F20 % glass-fiber-reinforced PC (improved flow)
- GF2110HI10 % glass-fiber-reinforced PC (toughened)
- GF2120HI20 % glass-fiber-reinforced PC (toughened)
- GF2130HI30 % glass-fiber-reinforced PC (toughened)
- FR1014SSilicone-based flame-retardant PC
- GL2012IRIR-transmissive black PC
Contact us
Tell us about the part, material requirements, equipment and expected volume. We will recommend suitable grades and the validation data you need.