mPPE compounds
FR93020N
- Prefix FR
- Flame retardant
- Series 93
- mPPE
- Filler 0
- Unfilled
- MVR 20
- 20 · 280 °C / 5 kg
- FR system N
- Halogen-free flame retardant
Halogen-free flame-retardant mPPE
- Planned grade
- Available
- GREENPOLYMER TDS
- V-0 @ 1.5 mmUL 94
- ≈ 15 cm³/10 minMelt volume-flow rate (MVR) · 280 °C / 5 kg
- ≈ 109 °CHDT · 1.80 MPa
Datasheet
Each value is shown with its test standard and conditions.
- DensityISO 11831.11g/cm³
- Melt volume-flow rate (MVR)ISO 1133 · 280 °C / 5 kg≈ 15cm³/10 min
- Tensile stress at yieldISO 527-1/-2≈ 72MPa
- Charpy notched impact strengthISO 179-1/1eA · 23 °C≈ 6kJ/m²
- Heat deflection temperatureISO 75-1/-2 · 1.80 MPa≈ 109°C
- Tensile modulusISO 527-1/-22.65GPa
- Flexural modulusISO 1782.6GPa
- Flexural strengthISO 178≈ 105MPa
- Vicat softening temperatureISO 306 · B120≈ 132°C
Flammability · UL 94Thickness (mm)
| 0.75 | 1.0 | 1.2 | 1.5 | 2.0 | 3.0 | |
|---|---|---|---|---|---|---|
| V-0 | V-0 @ 1.5 mm |
Typical values; not for use as specifications.
Processing window
- Drying93–99 °C, 3–4 h (8 h in total at most)
- Mold temperature71–93 °C
- Melt temperature260–288 °C
- ≤ 0.02 %Max. moisture before processing
- 0.5–0.7 % (in flow)Molding shrinkage
Colors
Colors
Natural and black; other colors matched to customer standards
Description
Halogen-free flame retardant, with low density, good dimensional stability and resistance to hydrolysis.
Key points
Used for
Related industries
Other grades in this family
Contact us
Tell us about the part, material requirements, equipment and expected volume. We will recommend suitable grades and the validation data you need.