mPPE compounds
GL93008
- Prefix GL
- General purpose (single resin, unfilled, non-flame-retardant)
- Series 93
- mPPE
- Filler 0
- Unfilled
- MVR 08
- 8 · 280 °C / 5 kg
General-purpose mPPE (unfilled, non-flame-retardant)
- Planned grade
- Available
- GREENPOLYMER TDS
- HB @ 1.5 mmUL 94
- 8 cm³/10 minMelt volume-flow rate (MVR) · 280 °C / 5 kg
- 115 °CHDT · 1.80 MPa
Datasheet
Each value is shown with its test standard and conditions.
- DensityISO 11831.06g/cm³
- Melt volume-flow rate (MVR)ISO 1133 · 280 °C / 5 kg8cm³/10 min
- Tensile modulusISO 527-1/-22.3GPa
- Tensile stress at yieldISO 527-1/-255MPa
- Elongation at breakISO 527-1/-230%
- Flexural strengthISO 17875MPa
- Charpy notched impact strengthISO 179-1/1eA · 23 °C15kJ/m²
- Heat deflection temperatureISO 75-1/-2 · 1.80 MPa115°C
- Heat deflection temperatureISO 75-1/-2 · 0.45 MPa130°C
- Vicat softening temperatureISO 306 · B120140°C
- Comparative tracking indexIEC 60112175V
Flammability · UL 94Thickness (mm)
| 0.75 | 1.0 | 1.2 | 1.5 | 2.0 | 3.0 | |
|---|---|---|---|---|---|---|
| HB | HB @ 1.5 mm |
Typical values; not for use as specifications.
Processing window
- Drying100–120 °C, 2–3 h
- Mold temperature80–120 °C
- Melt temperature280–300 °C
Colors
Colors
Natural and black; other colors matched to customer color standards
Description
Unfilled modified PPE with low density, dimensional stability, low water uptake and good heat resistance. Non-flame-retardant.