PA6 / PA66 compounds
GL40016X
- Prefix GL
- General purpose (single resin, unfilled, non-flame-retardant)
- Series 40
- PA6
- Filler 0
- Unfilled
- MVR 16
- 160 · 275 °C / 5 kg
- Property X
- Flow class ×10 (unfilled, flow value ≥ 100; the two digits × 10 give the flow value)
General-purpose PA6 (unfilled)
- Planned grade
- Available
- GREENPOLYMER TDS
- 60 °CHDT · 1.80 MPa
- 160 cm³/10 minMelt volume-flow rate (MVR) · 275 °C / 5 kg
Datasheet
Each value is shown with its test standard and conditions.
- DensityISO 11831.13g/cm³
- Melt volume-flow rate (MVR)ISO 1133 · 275 °C / 5 kg160cm³/10 min
- Tensile modulusISO 527-1/-2 · dry3.1GPa
- Tensile stress at yieldISO 527-1/-2 · dry80MPa
- Yield strainISO 527-1/-2 · dry3.8%
- Elongation at breakISO 527-1/-2 · dry24%
- Charpy notched impact strengthISO 179-1/1eA · 23 °C5.5kJ/m²
- Heat deflection temperatureISO 75-1/-2 · 1.80 MPa60°C
- Heat deflection temperatureISO 75-1/-2 · 0.45 MPa180°C
- Melting temperatureISO 11357-1/-3220°C
- Comparative tracking indexIEC 60112 · solution A600V
- Moisture absorptionISO 62 · 23 °C / 50 % RH equilibrium2.6–3.4%
Typical values; not for use as specifications.
Processing window
- Mold temperature40–60 °C
- Melt temperature250–270 °C
- 0.75 % (in flow and across flow, ISO 294-4)Molding shrinkage
Colors
Colors
Natural and black; other colors matched to customer color standards
Description
Unfilled injection-molding PA6 with good flow and toughness, easy to mold. Non-flame-retardant.
Key points
Used for
Other grades in this family
- FR40130Flame-retardant glass-fiber-reinforced PA6
- FR40320Flame-retardant carbon-fiber-reinforced PA6
- GF40320Carbon-fiber-reinforced PA6
- GF40130Glass-fiber-reinforced PA6 (GF30, non-flame-retardant)
- FR41130NHalogen-free flame-retardant glass-fiber-reinforced PA66
- GF41130Glass-fiber-reinforced PA66 (GF30)
- GL41012XGeneral-purpose PA66 (unfilled)
Contact us
Tell us about the part, material requirements, equipment and expected volume. We will recommend suitable grades and the validation data you need.