PA6 / PA66 compounds

GL41012X

Prefix GL: General purpose (single resin, unfilled, non-flame-retardant)
Series 41: PA66
Filler 0: Unfilled
MVR 12: 120 · 275 °C / 5 kg
Property X: Flow class ×10 (unfilled, flow value ≥ 100; the two digits × 10 give the flow value)

General-purpose PA66 (unfilled)

Planned grade
Available
GREENPOLYMER TDS

Add to sample tray Request a quote Request the TDS

75 °CHDT · 1.80 MPa

120 cm³/10 minMelt volume-flow rate (MVR) · 275 °C / 5 kg

Datasheet

Each value is shown with its test standard and conditions.

DensityISO 11831.13g/cm³
Melt volume-flow rate (MVR)ISO 1133 · 275 °C / 5 kg120cm³/10 min
Tensile modulusISO 527-1/-2 · dry3.0GPa
Tensile stress at yieldISO 527-1/-2 · dry85MPa
Yield strainISO 527-1/-2 · dry4.5%
Elongation at breakISO 527-1/-2 · dry30%
Charpy notched impact strengthISO 179-1/1eA · 23 °C5kJ/m²
Heat deflection temperatureISO 75-1/-2 · 1.80 MPa75°C
Heat deflection temperatureISO 75-1/-2 · 0.45 MPa220°C
Melting temperatureISO 11357-1/-3260°C
Comparative tracking indexIEC 60112 · solution A600V
Moisture absorptionISO 62 · 23 °C / 50 % RH equilibrium2.5–3.1%

Typical values; not for use as specifications.

Processing window

Mold temperature60–80 °C
Melt temperature280–300 °C
050100150200250300°C

1.50 % (in flow) / 1.80 % (across flow, ISO 294-4)Molding shrinkage

Colors

Colors

Natural and black; other colors matched to customer color standards

Description

Unfilled injection-molding PA66 with good flow and fast crystallization, balancing strength, stiffness and heat resistance. Non-flame-retardant.

Key points

Good flow, fast crystallization
Strength with stiffness
Heat and oil resistance

Used for

Cable ties
Connectors
Electrical structural parts
Small tool parts