POM compounds
GL92009
- Prefix GL
- General purpose (single resin, unfilled, non-flame-retardant)
- Series 92
- POM
- Filler 0
- Unfilled
- MFR 09
- 9 · 190 °C / 2.16 kg
General-purpose copolymer POM
- Planned grade
- Available
- GREENPOLYMER TDS
- HB @ 1.5 mmUL 94
- 7–12 g/10 minMelt mass-flow rate (MFR) · 190 °C / 2.16 kg
- 90–105 °CHDT · 1.80 MPa
Datasheet
Each value is shown with its test standard and conditions.
- DensityISO 11831.39–1.42g/cm³
- Melt mass-flow rate (MFR)ISO 1133 · 190 °C / 2.16 kg7–12g/10 min
- Tensile strengthISO 527-1/-260–68MPa
- Charpy notched impact strengthISO 179-1/1eA · 23 °C5–8kJ/m²
- Heat deflection temperatureISO 75-1/-2 · 1.80 MPa90–105°C
- Flexural modulusISO 1782.4–2.9GPa
Flammability · UL 94Thickness (mm)
| 0.75 | 1.0 | 1.2 | 1.5 | 2.0 | 3.0 | |
|---|---|---|---|---|---|---|
| HB | HB @ 1.5 mm |
Typical values; not for use as specifications.
Processing window
- Drying120–140 °C, 3–4 h (if moist)
- Mold temperature80–120 °C
- Melt temperature190–210 °C
- ≤ 0.15 %Max. moisture before processing
- 1.8–2.0 %Molding shrinkage
Colors
Colors
Natural and black; other colors matched to customer standards
Description
Wear resistant and self-lubricating, with good dimensional and thermal stability.