POM compounds
GL92024
- Prefix GL
- General purpose (single resin, unfilled, non-flame-retardant)
- Series 92
- POM
- Filler 0
- Unfilled
- MVR 24
- 24 · 190 °C / 2.16 kg
High-flow copolymer POM
- Planned grade
- Available
- GREENPOLYMER TDS
- HB @ 1.5 mmUL 94
- 24 cm³/10 minMelt volume-flow rate (MVR) · 190 °C / 2.16 kg
- 106 °CHDT · 1.80 MPa
Datasheet
Each value is shown with its test standard and conditions.
- DensityISO 11831.41g/cm³
- Melt volume-flow rate (MVR)ISO 1133 · 190 °C / 2.16 kg24cm³/10 min
- Tensile modulusISO 527-1/-22.9GPa
- Tensile stress at yieldISO 527-1/-265MPa
- Yield strainISO 527-1/-27.5%
- Elongation at breakISO 527-1/-217%
- Charpy notched impact strengthISO 179-1/1eA · 23 °C5.5kJ/m²
- Heat deflection temperatureISO 75-1/-2 · 1.80 MPa106°C
Flammability · UL 94Thickness (mm)
| 0.75 | 1.0 | 1.2 | 1.5 | 2.0 | 3.0 | |
|---|---|---|---|---|---|---|
| HB | HB @ 1.5 mm |
Typical values; not for use as specifications.
Processing window
- Drying120–140 °C, 3–4 h
- Mold temperature80–120 °C
- Melt temperature190–210 °C
- 1.9 % (in flow) / 1.8 % (across flow, ISO 294-4)Molding shrinkage
Colors
Colors
Natural and black; other colors matched to customer color standards
Description
High-flow copolymer POM for thin walls and multi-cavity molds, with wear resistance, self-lubrication and dimensional stability.