PP compounds
GF90130
- Prefix GF
- Reinforced / filled (non-flame-retardant)
- Series 90
- PP
- Filler 1
- Glass fiber
- Filler content 30
- 30 %
Glass-fiber-reinforced PP (GF30, chemically coupled)
- Planned grade
- Available
- GREENPOLYMER TDS
- HBUL 94
- ≈ 5 g/10 minMelt mass-flow rate (MFR) · 230 °C / 2.16 kg
- 140–150 °CHDT · 1.80 MPa
Datasheet
Each value is shown with its test standard and conditions.
- Glass-fiber content—30%
- DensityISO 11831.10–1.13g/cm³
- Melt mass-flow rate (MFR)ISO 1133 · 230 °C / 2.16 kg≈ 5g/10 min
- Tensile stress at breakISO 527-1/-280–88MPa
- Tensile modulusISO 527-1/-26.0–7.0GPa
- Charpy notched impact strengthISO 179-1/1eA · 23 °C8–10kJ/m²
- Charpy notched impact strengthISO 179-1/1eA · −30 °C7–9kJ/m²
- Heat deflection temperatureISO 75-1/-2 · 1.80 MPa140–150°C
Typical values; not for use as specifications.
Processing window
- DryingUsually not needed; if moist, 80–100 °C, 2–4 h
- Mold temperature15–60 °C
- Melt temperature210–270 °C
- — (PP does not absorb moisture)Max. moisture before processing
- 0.4 % (in flow) / 0.7 % (across flow)Molding shrinkage
Colors
Colors
Natural and black; other colors matched to customer standards
Description
Combines low density with high stiffness; an alternative to engineering plastics in some structural parts.