Bio-based materials
GF43130B50
- Prefix GF
- Reinforced / filled (non-flame-retardant)
- Series 43
- PA610
- Filler 1
- Glass fiber
- Filler content 30
- 30 %
- Bio-based content B50
- Bio-based carbon ≥ 50 %
Bio-based glass-fiber-reinforced PA610 (GF30)
- Planned grade
- Available
- GREENPOLYMER TDS
- HB @ 1.5 mmUL 94
- 200–215 °CHDT · 1.80 MPa
- ≥ 50 %Bio-based carbon content
Datasheet
Each value is shown with its test standard and conditions.
- DensityISO 11831.30–1.35g/cm³
- Tensile strengthISO 527-1/-2 · dry140–170MPa
- Flexural modulusISO 178 · dry7.0–8.5GPa
- Charpy notched impact strengthISO 179-1/1eA · 23 °C; dry9–14kJ/m²
- Heat deflection temperatureISO 75-1/-2 · 1.80 MPa200–215°C
Flammability · UL 94Thickness (mm)
| 0.75 | 1.0 | 1.2 | 1.5 | 2.0 | 3.0 | |
|---|---|---|---|---|---|---|
| HB | HB @ 1.5 mm |
Typical values; not for use as specifications.
Content and colors
Bio-based carbon content
≥ 50 %
Share of total organic carbon (ASTM D6866)
Composition
PA610 (sebacic acid from castor oil) with 30 % glass fiber
Colors
Natural and black; other colors matched to customer standards
Description
PA610 (sebacic acid from castor oil) with 30 % glass fiber. Absorbs less moisture than PA6 / PA66 and stays dimensionally stable.
Key points
Used for
Other grades in this family
- GF42130B35Bio-based glass-fiber-reinforced PA56 (GF30)
- FR42130NB30Bio-based halogen-free flame-retardant glass-fiber-reinforced PA56
- GL44005EXB90Bio-based PA1010 extrusion compound
- GB07025B20Bio-based PC/PLA alloy
- FR07025NB20Bio-based halogen-free flame-retardant PC/PLA alloy
- GL91011B80Bio-based PE injection-molding compound
- GF90420B20Plant-fiber-filled PP
Contact us
Tell us about the part, material requirements, equipment and expected volume. We will recommend suitable grades and the validation data you need.