Bio-based materials
GF90420B20
- Prefix GF
- Reinforced / filled (non-flame-retardant)
- Series 90
- PP
- Filler 4
- Plant fiber
- Filler content 20
- 20 %
- Bio-based content B20
- Bio-based carbon ≥ 20 %
Plant-fiber-filled PP
- Planned grade
- Available
- GREENPOLYMER TDS
- HB @ 1.5 mmUL 94
- 60–75 °CHDT · 1.80 MPa
- ≥ 20 %Bio-based carbon content
- 5–20 g/10 minMelt mass-flow rate (MFR) · 230 °C / 2.16 kg
Datasheet
Each value is shown with its test standard and conditions.
- DensityISO 11830.98–1.08g/cm³
- Melt mass-flow rate (MFR)ISO 1133 · 230 °C / 2.16 kg5–20g/10 min
- Tensile strengthISO 527-1/-225–35MPa
- Flexural modulusISO 1782.0–3.0GPa
- Charpy notched impact strengthISO 179-1/1eA · 23 °C3–6kJ/m²
- Heat deflection temperatureISO 75-1/-2 · 1.80 MPa60–75°C
Flammability · UL 94Thickness (mm)
| 0.75 | 1.0 | 1.2 | 1.5 | 2.0 | 3.0 | |
|---|---|---|---|---|---|---|
| HB | HB @ 1.5 mm |
Typical values; not for use as specifications.
Content and colors
Bio-based carbon content
≥ 20 %
Share of total organic carbon (ASTM D6866)
Composition
PP with 20–30 % bamboo, straw or hemp fiber and compatibilizer
Colors
Natural and black; other colors matched to customer standards
Description
PP with 20–30 % bamboo, straw or hemp fiber and compatibilizer. A natural texture without painting, and a lower density than mineral-filled PP.
Key points
Used for
Other grades in this family
- GF42130B35Bio-based glass-fiber-reinforced PA56 (GF30)
- FR42130NB30Bio-based halogen-free flame-retardant glass-fiber-reinforced PA56
- GF43130B50Bio-based glass-fiber-reinforced PA610 (GF30)
- GL44005EXB90Bio-based PA1010 extrusion compound
- GB07025B20Bio-based PC/PLA alloy
- FR07025NB20Bio-based halogen-free flame-retardant PC/PLA alloy
- GL91011B80Bio-based PE injection-molding compound
Contact us
Tell us about the part, material requirements, equipment and expected volume. We will recommend suitable grades and the validation data you need.