Biodegradable materials
GL00010FBD
- Prefix GL
- General purpose (single resin, unfilled, non-flame-retardant)
- Series 00
- PLA
- Filler 0
- Unfilled
- MFR 10
- 10 · 210 °C / 2.16 kg
- Process FB
- Fiber / monofilament / filament-feedstock grade
- Biodegradable D
- Designed to be fully biodegradable
Biodegradable PLA filament and fiber compound
- Planned grade
- Available
- GREENPOLYMER TDS
- 52–58 °CHDT · 0.45 MPa
- 4–15 g/10 minMelt mass-flow rate (MFR) · 210 °C / 2.16 kg
Datasheet
Each value is shown with its test standard and conditions.
- DensityISO 11831.24–1.26g/cm³
- Melt mass-flow rate (MFR)ISO 1133 · 210 °C / 2.16 kg4–15g/10 min
- Tensile strengthISO 527-1/-250–65MPa
- Flexural modulusISO 1783.2–3.7GPa
- Heat deflection temperatureISO 75-1/-2 · 0.45 MPa52–58°C
Typical values; not for use as specifications.
Processing window
Process: monofilament / 3D-printing filament / fiber spinning
- Drying100 °C, 4–6 h, desiccant dryer (dew point ≤ −40 °C), moisture < 250 ppm
- Mold temperature25 °C
- Melt temperature200–205 °C
- ≤ 0.025 %Max. moisture before processing
Colors
Biodegradation performance is subject to third-party testing and certification
Composition
PLA ≥ 90 %, diameter-stability and lubricating aids
Colors
Natural; colors assessed per project (masterbatch must meet the same degradation and heavy-metal requirements)
Description
PLA ≥ 90 %, diameter-stability and lubricating aids. Extrudes consistently; for 3D-printing filament and nonwovens.
Key points
Used for
Other grades in this family
- GB02004BFDBiodegradable PBAT/PLA blown-film compound
- GL01004BFDBiodegradable PBAT mulch-film compound
- GB03004BFDBiodegradable starch-based blown-film compound
- GL00020DBiodegradable PLA injection-molding compound (general purpose)
- GL00017HTDBiodegradable heat-resistant PLA injection-molding compound
- GL00012HIDBiodegradable toughened PLA injection-molding compound
- GL00006SHDBiodegradable PLA sheet-extrusion compound
- GL04015DBiodegradable PBS injection-molding compound
- GL05012DBiodegradable PHA injection-molding compound
- GL00005FODBiodegradable PLA foaming compound
- GL06007DBiodegradable PCL low-temperature forming compound
Contact us
Tell us about the part, material requirements, equipment and expected volume. We will recommend suitable grades and the validation data you need.