Biodegradable materials
GL06007D
- Prefix GL
- General purpose (single resin, unfilled, non-flame-retardant)
- Series 06
- PCL
- Filler 0
- Unfilled
- MFR 07
- 7 · 160 °C / 2.16 kg
- Biodegradable D
- Designed to be fully biodegradable
Biodegradable PCL low-temperature forming compound
- Planned grade
- Available
- GREENPOLYMER TDS
- 5–10 g/10 minMelt mass-flow rate (MFR) · 160 °C / 2.16 kg
Datasheet
Each value is shown with its test standard and conditions.
- DensityISO 11831.10–1.15g/cm³
- Melt mass-flow rate (MFR)ISO 1133 · 160 °C / 2.16 kg5–10g/10 min
- Tensile strengthISO 527-1/-215–30MPa
- Flexural modulusISO 1780.3–0.5GPa
- Melting temperatureISO 11357-358–62°C
Typical values; not for use as specifications.
Colors
Biodegradation performance is subject to third-party testing and certification
Composition
PCL ≥ 90 %
Colors
Natural; colors assessed per project (masterbatch must meet the same degradation and heavy-metal requirements)
Description
PCL ≥ 90 %. A low melting point (about 60 °C); used to modify other biodegradable compounds.
Key points
Used for
Other grades in this family
- GB02004BFDBiodegradable PBAT/PLA blown-film compound
- GL01004BFDBiodegradable PBAT mulch-film compound
- GB03004BFDBiodegradable starch-based blown-film compound
- GL00020DBiodegradable PLA injection-molding compound (general purpose)
- GL00017HTDBiodegradable heat-resistant PLA injection-molding compound
- GL00012HIDBiodegradable toughened PLA injection-molding compound
- GL00006SHDBiodegradable PLA sheet-extrusion compound
- GL04015DBiodegradable PBS injection-molding compound
- GL05012DBiodegradable PHA injection-molding compound
- GL00005FODBiodegradable PLA foaming compound
- GL00010FBDBiodegradable PLA filament and fiber compound