PBT / PET (flame-retardant and reinforced)
GF80130
- Prefix GF
- Reinforced / filled (non-flame-retardant)
- Series 80
- PBT
- Filler 1
- Glass fiber
- Filler content 30
- 30 %
Glass-fiber-reinforced PBT (GF30)
- Planned grade
- Available
- GREENPOLYMER TDS
- HB @ 1.5 mmUL 94
- ≈ 5.5 cm³/10 minMelt volume-flow rate (MVR) · 250 °C / 2.16 kg
- 205–215 °CHDT · 1.80 MPa
Datasheet
Each value is shown with its test standard and conditions.
- Glass-fiber content—30%
- DensityISO 11831.51–1.53g/cm³
- Melt volume-flow rate (MVR)ISO 1133 · 250 °C / 2.16 kg≈ 5.5cm³/10 min
- Tensile modulusISO 527-1/-210.0GPa
- Charpy notched impact strengthISO 179-1/1eA · 23 °C11kJ/m²
- Heat deflection temperatureISO 75-1/-2 · 1.80 MPa205–215°C
- Heat deflection temperatureISO 75-1/-2 · 0.45 MPa≈ 220°C
- Tensile stress at breakISO 527-1/-2135–140MPa
- Elongation at breakISO 527-1/-22.5–2.7%
- Flexural modulusISO 1788.8–9.0GPa
Flammability · UL 94Thickness (mm)
| 0.75 | 1.0 | 1.2 | 1.5 | 2.0 | 3.0 | |
|---|---|---|---|---|---|---|
| HB | HB @ 1.5 mm |
Typical values; not for use as specifications.
Processing window
- Drying80–120 °C, 4 h
- Mold temperature60–100 °C
- Melt temperature250–275 °C
- ≤ 0.04 %Max. moisture before processing
- 0.5 % (flow) / 1.3 % (transverse)Molding shrinkage
Colors
Colors
Natural and black; other colors matched to customer standards
Description
Stiff, dimensionally stable, good electrical insulation, non-flame-retardant.