PBT / PET (flame-retardant and reinforced)
GL80015
- Prefix GL
- General purpose (single resin, unfilled, non-flame-retardant)
- Series 80
- PBT
- Filler 0
- Unfilled
- MVR 15
- 15 · 250 °C / 2.16 kg
General-purpose PBT (unfilled)
- Planned grade
- Available
- GREENPOLYMER TDS
- HB @ 1.5 mmUL 94
- 10–19 cm³/10 minMelt volume-flow rate (MVR) · 250 °C / 2.16 kg
- 50–60 °CHDT · 1.80 MPa
Datasheet
Each value is shown with its test standard and conditions.
- DensityISO 11831.30g/cm³
- Melt volume-flow rate (MVR)ISO 1133 · 250 °C / 2.16 kg10–19cm³/10 min
- Tensile modulusISO 527-1/-22.5–2.6GPa
- Tensile stress at yieldISO 527-1/-257–60MPa
- Yield strainISO 527-1/-23.7–4.0%
- Elongation at breakISO 527-1/-2> 50%
- Flexural modulusISO 1782.3–2.4GPa
- Charpy notched impact strengthISO 179-1/1eA · 23 °C5–6kJ/m²
- Heat deflection temperatureISO 75-1/-2 · 1.80 MPa50–60°C
- Comparative tracking indexIEC 60112 · solution A550–600V
Flammability · UL 94Thickness (mm)
| 0.75 | 1.0 | 1.2 | 1.5 | 2.0 | 3.0 | |
|---|---|---|---|---|---|---|
| HB | HB @ 1.5 mm |
Typical values; not for use as specifications.
Processing window
- Drying100–120 °C, 4 h
- Mold temperature40–80 °C
- Melt temperature250–270 °C
- 1.5–1.7 % (in flow, ISO 294-4)Molding shrinkage
Colors
Colors
Natural and black; other colors matched to customer standards
Description
Unfilled injection-molding PBT. Crystallizes fast, resists chemicals, and offers good electrical insulation and dimensional stability. Non-flame-retardant.