PBT / PET (flame-retardant and reinforced)
FR80130CT
- Prefix FR
- Flame retardant
- Series 80
- PBT
- Filler 1
- Glass fiber
- Filler content 30
- 30 %
- Property CT
- High CTI
Flame-retardant glass-fiber-reinforced PBT (high CTI)
- Planned grade
- Available
- GREENPOLYMER TDS
- V-0 @ 1.5 mmUL 94
- 10–25 g/10 minMelt mass-flow rate (MFR) · 250 °C / 2.16 kg
- 200–215 °CHDT · 1.80 MPa
Datasheet
Each value is shown with its test standard and conditions.
- DensityISO 11831.55–1.70g/cm³
- Melt mass-flow rate (MFR)ISO 1133 · 250 °C / 2.16 kg10–25g/10 min
- Tensile strengthISO 527-1/-2100–130MPa
- Charpy notched impact strengthISO 179-1/1eA · 23 °C6–10kJ/m²
- Heat deflection temperatureISO 75-1/-2 · 1.80 MPa200–215°C
- Flexural modulusISO 1788–10GPa
- Comparative tracking index (CTI)IEC 60112≥ 600V
Flammability · UL 94Thickness (mm)
| 0.75 | 1.0 | 1.2 | 1.5 | 2.0 | 3.0 | |
|---|---|---|---|---|---|---|
| V-0 | V-0 @ 1.5 mm |
Typical values; not for use as specifications.
Processing window
- Drying80–120 °C, 4 h
- Mold temperature60–100 °C
- Melt temperature250–275 °C
- ≤ 0.04 %Max. moisture before processing
- 0.5 % (flow) / 1.3 % (transverse)Molding shrinkage
Colors
Colors
Natural and black; other colors matched to customer standards
Description
Flame retardant, with good electrical insulation and a high comparative tracking index (CTI).