PC/ABS compounds
GB5110
- Prefix GB
- Alloy / blend (non-flame-retardant)
- Series 5
- PC/ABS
- Filler 1
- Glass fiber
- Filler content 10
- 10 %
10 % glass-fiber-reinforced PC/ABS
- Planned grade
- Available
- GREENPOLYMER TDS
- HBUL 94
- 16 cm³/10 minMelt volume-flow rate (MVR) · 260 °C / 5 kg
- ≈ 121 °CHDT · 1.80 MPa
Datasheet
Each value is shown with its test standard and conditions.
- Glass-fiber content—10%
- DensityISO 11831.20–1.24g/cm³
- Melt volume-flow rate (MVR)ISO 1133 · 260 °C / 5 kg16cm³/10 min
- Tensile modulusISO 527-1/-24.8GPa
- Izod notched impact strengthISO 180/1A · 23 °C≈ 8kJ/m²
- Heat deflection temperatureISO 75-1/-2 · 1.80 MPa≈ 121°C
- Tensile stress at breakISO 527-1/-2≈ 95MPa
- Elongation at breakISO 527-1/-2≈ 3.7%
- Vicat softening temperatureISO 306 · B120≈ 134°C
- Comparative tracking indexIEC 60112 · solution A200V
Typical values; not for use as specifications.
Processing window
- Drying95–110 °C, 4 h, desiccant dryer
- Mold temperature70–90 °C
- Melt temperature230–275 °C (usually 270 °C)
- ≤ 0.02 %Max. moisture before processing
- 0.25–0.45 % (in flow) / 0.35–0.55 % (across flow)Molding shrinkage
Colors
Colors
Natural and black; other colors matched to customer standards
Description
Glass-fiber-reinforced PC/ABS with higher stiffness and dimensional stability.
Key points
Used for
Other grades in this family
- GB5020General-purpose PC/ABS (MVR 20)
- GB5020UPC/ABS (UV-stabilized, MVR 20)
- GB5018General-purpose PC/ABS (MVR 18)
- GB5018UPC/ABS (UV-stabilized, MVR 18)
- GB5012PGPC/ABS (plating grade)
- GB512020 % glass-fiber-reinforced PC/ABS
- GB51055 % glass-fiber-reinforced PC/ABS
- GB511515 % glass-fiber-reinforced PC/ABS
- GB512525 % glass-fiber-reinforced PC/ABS
- GB5020ASPC/ABS (antistatic)
- GB5020HGPC/ABS (high gloss)
- GB5017HTHeat-resistant PC/ABS
- GB5015L30Low-temperature high-impact PC/ABS
Contact us
Tell us about the part, material requirements, equipment and expected volume. We will recommend suitable grades and the validation data you need.